Evolution Powder-free Latex Examination Gloves

Evolution Powder-free Latex Examination Gloves

• Secure-Grip™ textured surface ensures better handling even when wet


• Superior ease of donning


• Micro-Contouring™ varies glove thickness for maximum sensitivity
These latex gloves are made from medium modulus natural latex. They exceed ASTM D3578-91 (reapproved 1988) standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%. Evolution One™ Powder Free Latex Exam Gloves


These latex gloves provide superior protection while allowing outstanding gripping power. Available in five sizes and supplied in a box of 100. Non-sterile.

Item# Description U.S. List Price Quantity
60-5165 Evolution One™ Latex Exam Gloves, X-Large, box of 100
60-5164 Evolution One™ Latex Exam Gloves, Large, box of 100
60-5163 Evolution One™ Latex Exam Gloves, Medium, box of 100
60-5162 Evolution One™ Latex Exam Gloves, Small, box of 100
60-5161 Evolution One™ Latex Exam Gloves, X-Small, box of 100
Login for U.S. Pricing
• Secure-Grip™ textured surface ensures better handling even when wet


• Superior ease of donning


• Micro-Contouring™ varies glove thickness for maximum sensitivity
These latex gloves are made from medium modulus natural latex. They exceed ASTM D3578-91 (reapproved 1988) standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%. Evolution One™ Powder Free Latex Exam Gloves


These latex gloves provide superior protection while allowing outstanding gripping power. Available in five sizes and supplied in a box of 100. Non-sterile.
Specifications60-516560-516460-516360-516260-5161
CertificationsASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105DASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105DASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105DASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105DASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D
CuffBeadedBeadedBeadedBeadedBeaded
Cuff Thickness Metric3.2 to 6.3 mils3.2 to 6.3 mils3.2 to 6.3 mils3.2 to 6.3 mils3.2 to 6.3 mils
Elasticity/Elongation After Aging500% min.500% min.500% min.500% min.500% min.
Elasticity/Elongation Before Aging700% min.700% min.700% min.700% min.700% min.
Finger Thickness Metric7.1 to 10.2 mils7.1 to 10.2 mils7.1 to 10.2 mils7.1 to 10.2 mils7.1 to 10.2 mils
Inner Surface CoatingPowder-freePowder-freePowder-freePowder-freePowder-free
Length Metric245 mm (245 mm (245 mm (245 mm (245 mm (
MaterialNatural Rubber LatexNatural Rubber LatexNatural Rubber LatexNatural Rubber LatexNatural Rubber Latex
Outer SurfaceTexturedTexturedTexturedTexturedTextured
Palm Thickness Metric5.1 to 8.3 mils5.1 to 8.3 mils5.1 to 8.3 mils5.1 to 8.3 mils5.1 to 8.3 mils
SizeX-LargeLargeMediumSmallX-Small
SterilityNon-SterileNon-SterileNon-SterileNon-SterileNon-Sterile
Tensile Strength After Aging16 Mpa min.16 Mpa min.16 Mpa min.16 Mpa min.16 Mpa min.
Tensile Strength Before Aging21 Mpa min.21 Mpa min.21 Mpa min.21 Mpa min.21 Mpa min.