Synetron Powder-free Latex Examination Gloves
These latex gloves are made from medium modulus natural latex. They exceed ASTM D3578-91 standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%. Synetron™ Powder Free Latex Gloves These outstanding latex gloves provide hand protection while allowing superior gripping power.
- Accu-Grip™ micro-roughened surface provides extra gripping power even when wet
- Superior ease of donning compared to other powder free latex gloves
- Micro-Contouring™ varies glove thickness for maximum sensitivity
- Available in four sizes
- Supplied in a box of 50. Non-sterile
These latex gloves are made from medium modulus natural latex. They exceed ASTM D3578-91 standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%. Synetron™ Powder Free Latex Gloves These outstanding latex gloves provide hand protection while allowing superior gripping power.
- Accu-Grip™ micro-roughened surface provides extra gripping power even when wet
- Superior ease of donning compared to other powder free latex gloves
- Micro-Contouring™ varies glove thickness for maximum sensitivity
- Available in four sizes
- Supplied in a box of 50. Non-sterile
| Specifications | 60-5157 | 60-5160 | 60-5159 | 60-5158 |
|---|---|---|---|---|
| Certifications | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D |
| Cuff | Beaded | Beaded | Beaded | Beaded |
| Cuff Thickness Metric | 7.9 mils | 7.9 mils | 7.9 mils | 7.9 mils |
| Elasticity/Elongation After Aging | 500% min. | 500% min. | 500% min. | 500% min. |
| Elasticity/Elongation Before Aging | 700% min. | 700% min. | 700% min. | 700% min. |
| Finger Thickness Metric | 13.8 mils | 13.8 mils | 13.8 mils | 13.8 mils |
| Inner Surface Coating | Powder-free | Powder-free | Powder-free | Powder-free |
| Length Metric | 290 mm | 290 mm | 290 mm | 290 mm |
| Material | Natural Rubber Latex | Natural Rubber Latex | Natural Rubber Latex | Natural Rubber Latex |
| Outer Surface | Textured | Textured | Textured | Textured |
| Palm Thickness Metric | 10.6 mils | 10.6 mils | 10.6 mils | 10.6 mils |
| Size | Small | X-Large | Large | Medium |
| Sterility | Non-Sterile | Non-Sterile | Non-Sterile | Non-Sterile |
| Tensile Strength After Aging | 16 Mpa min. | 16 Mpa min. | 16 Mpa min. | 16 Mpa min. |
| Tensile Strength Before Aging | 21 Mpa min. | 21 Mpa min. | 21 Mpa min. | 21 Mpa min. |