Evolution Powder-free Latex Examination Gloves
These latex gloves provide superior protection while allowing outstanding gripping power. They are made from medium modulus natural latex. They exceed ASTM D3578-91 standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%.
- Secure-Grip™ textured surface ensures better handling even when wet
- Superior ease of donning
- Micro-Contouring™ varies glove thickness for maximum sensitivity
- Available in five sizes and supplied in a box of 100. Non-sterile.
These latex gloves provide superior protection while allowing outstanding gripping power. They are made from medium modulus natural latex. They exceed ASTM D3578-91 standards for major defects. Sampled in accordance with MILS STD 105D. They have a tensile strength before aging minimum of 21 MPa; after aging minimum of 16 MPa. Elongation properties before aging minimum of 700%; after aging minimum of 500%.
- Secure-Grip™ textured surface ensures better handling even when wet
- Superior ease of donning
- Micro-Contouring™ varies glove thickness for maximum sensitivity
- Available in five sizes and supplied in a box of 100. Non-sterile.
Specifications | 60-5165 | 60-5164 | 60-5163 | 60-5162 | 60-5161 |
---|---|---|---|---|---|
Certifications | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D | ASTM D3578-91 (reapproved 1988), Sampled in accordance with MILS STD 105D |
Cuff | Beaded | Beaded | Beaded | Beaded | Beaded |
Cuff Thickness Metric | 3.2 to 6.3 mils | 3.2 to 6.3 mils | 3.2 to 6.3 mils | 3.2 to 6.3 mils | 3.2 to 6.3 mils |
Elasticity/Elongation After Aging | 500% min. | 500% min. | 500% min. | 500% min. | 500% min. |
Elasticity/Elongation Before Aging | 700% min. | 700% min. | 700% min. | 700% min. | 700% min. |
Finger Thickness Metric | 7.1 to 10.2 mils | 7.1 to 10.2 mils | 7.1 to 10.2 mils | 7.1 to 10.2 mils | 7.1 to 10.2 mils |
Inner Surface Coating | Powder-free | Powder-free | Powder-free | Powder-free | Powder-free |
Length Metric | 245 mm | 245 mm | 245 mm | 245 mm | 245 mm |
Material | Natural Rubber Latex | Natural Rubber Latex | Natural Rubber Latex | Natural Rubber Latex | Natural Rubber Latex |
Outer Surface | Textured | Textured | Textured | Textured | Textured |
Palm Thickness Metric | 5.1 to 8.3 mils | 5.1 to 8.3 mils | 5.1 to 8.3 mils | 5.1 to 8.3 mils | 5.1 to 8.3 mils |
Size | X-Large | Large | Medium | Small | X-Small |
Sterility | Non-Sterile | Non-Sterile | Non-Sterile | Non-Sterile | Non-Sterile |
Tensile Strength After Aging | 16 Mpa min. | 16 Mpa min. | 16 Mpa min. | 16 Mpa min. | 16 Mpa min. |
Tensile Strength Before Aging | 21 Mpa min. | 21 Mpa min. | 21 Mpa min. | 21 Mpa min. | 21 Mpa min. |