Neopro Chloroprene Powder-free Examination Gloves
NeoPro is a proprietary formulation of completely synthetic polymers. This unique glove combines the barrier performance of a synthetic with the superior comfort typically found in natural latex. Powder-free NeoPro also provides exceptional tactile sensitivity and is textured for a more secure grip.
- Powder-free chloroprene examination gloves
- Help reduce the risk of skin irritation or contamination by glove powders
- The barrier performance of a completely synthetic glove with the fit and feel typical of natural latex
- Beaded, tear-resistant cuffs
- Textured for secure grip
NeoPro is a proprietary formulation of completely synthetic polymers. This unique glove combines the barrier performance of a synthetic with the superior comfort typically found in natural latex. Powder-free NeoPro also provides exceptional tactile sensitivity and is textured for a more secure grip.
- Powder-free chloroprene examination gloves
- Help reduce the risk of skin irritation or contamination by glove powders
- The barrier performance of a completely synthetic glove with the fit and feel typical of natural latex
- Beaded, tear-resistant cuffs
- Textured for secure grip
These gloves are ambidextrous, non-sterile, and are intended for single time use only. They are available in five sizes are supplied 100 per dispenser box (by weight).
Specifications | 72-3409 | 72-3408 | 72-3407 | 72-3406 | 72-3405 |
---|---|---|---|---|---|
Cuff | Beaded | Beaded | Beaded | Beaded | Beaded |
Cuff Thickness Metric | 4.1 mils | 4.1 mils | 4.1 mils | 4.1 mils | 4.1 mils |
Elasticity/Elongation After Aging | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) |
Elasticity/Elongation Before Aging | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) | 500% min. (ASTM 300% min.) |
Finger Thickness Metric | 6.4 mils (ASTM 1.97 min.) | 6.4 mils (ASTM 1.97 min.) | 6.4 mils (ASTM 1.97 min.) | 6.4 mils (ASTM 1.97 min.) | 6.4 mils (ASTM 1.97 min.) |
Inner Surface Coating | Powder-free | Powder-free | Powder-free | Powder-free | Powder-free |
Length English | 10 in | 10 in | 10 in | 10 in | 10 in |
Length Metric | 250 mils min. (ASTM 230 min.) | 250 mils min. (ASTM 230 min.) | 250 mils min. (ASTM 230 min.) | 250 mils min. (ASTM 230 min.) | 250 mils min. (ASTM 230 min.) |
Material | Chloroprene; not made from natural rubber latex | Chloroprene; not made from natural rubber latex | Chloroprene; not made from natural rubber latex | Chloroprene; not made from natural rubber latex | Chloroprene; not made from natural rubber latex |
Outer Surface | Textured | Textured | Textured | Textured | Textured |
Palm Thickness Metric | 4.7 mils (ASTM 3.15 min.) | 4.7 mils (ASTM 3.15 min.) | 4.7 mils (ASTM 3.15 min.) | 4.7 mils (ASTM 3.15 min.) | 4.7 mils (ASTM 3.15 min.) |
Shape | Ambidextrous | Ambidextrous | Ambidextrous | Ambidextrous | Ambidextrous |
Size | X-Large | Large | Medium | Small | X-Small |
Sterility | Non-Sterile | Non-Sterile | Non-Sterile | Non-Sterile | Non-Sterile |
Tensile Strength After Aging | 19 Mpa (ASTM 9 min.) | 19 Mpa (ASTM 9 min.) | 19 Mpa (ASTM 9 min.) | 19 Mpa (ASTM 9 min.) | 19 Mpa (ASTM 9 min.) |
Tensile Strength Before Aging | 16 Mpa (ASTM 9 min.) | 16 Mpa (ASTM 9 min.) | 16 Mpa (ASTM 9 min.) | 16 Mpa (ASTM 9 min.) | 16 Mpa (ASTM 9 min.) |